【Filar Guide】Ceramic rod
- Fields：
- １、Bright silk
- ２、Black silk
- ３、Shaped wire
- ４、NanoRed wire
- ５、Litan wire
- Key Advantages:
- 1. Reduces dust generation
- 2. Minimizes filament fuzz and stray fibers
- 3. Excellent wear resistance with extended service life
- 4. Reduces waste caused by frequent component replacement
Aluminum oxide (Al2O3)
Aluminum oxide is a typical amphoteric oxide, which appears as a white solid that is insoluble in water. It has the characteristics of high mechanical strength, non-toxicity, odorlessness, and insolubility in non-polar organic solvents such as water and ethanol. Because it is slightly soluble in acid and alkali and can dissolve in inorganic acid and alkaline solutions, aluminum oxide plays an important role in chemical reactions. In addition, the relative density of aluminum oxide is 4.0, and its melting point is as high as 2050℃, giving it high temperature stability.
Alumina ceramic is a high-tech ceramic product with excellent performance, and it emerged in the ceramic industry due to its comprehensive technical advantages. Alumina ceramic has outstanding properties such as high mechanical strength, large hardness, low high-frequency dielectric loss, high-temperature insulation resistance, chemical corrosion resistance, and good thermal conductivity. In addition, alumina ceramic has uniform particle size, smooth surface, white spherical porous particles, and can be applied in various industrial fields.
This spinning component is made from high-quality alumina nanometer powder and incorporates a unique wear-resistant formula. This special design not only greatly improves productivity, but also ensures the durability of the product, particularly under high load, high speed, and high temperature conditions. Therefore, you can use our products with confidence and enjoy long-term stable benefits.
On-Machine Test Duration: 13 Days (Continuous Use Without Replacing New Parts) Total: 36 Days
Filament Type: 90/24 Nylon Black Yarn
After 36 days of operation, microscopic examination shows that the nozzle shows no significant wear.
Aluminum oxide Al2O3 (99.5%)
| Item | Unit | Test Standard |
|---|---|---|
| Density | g/cm3 | 3.92 |
| Elastic Modulus | Gpa | 340 |
| Coefficient of thermal | 10-6K-1 | 8.5 |
| hardness (HV) | Mpa | 1650 |
| Fracture toughness | Mpa | 4.2 |
| Flexural Strength (room temperature) | Mpa | 310 |
| Flexural Strength (700℃) | Mpa | 230 |
| Bending strength (room temperature) | Mpa | 2200 |
| Thermal conductivity | W (mk)-1 | 26 |
| specific resistivity | ≥1016 | |
| Maximum operating temperature (no load) | ℃ | 1750 |
| Acid and alkali corrosion resistance | strong |